Project
Development of a micromechanics based damage law for the hydrogen induced ductile failure of notched components in high-strength low alloy steel
Information
Project Team
Outputs and Outcomes
Publications
Hydrogen-assisted toughness reduction of a 42CrMo4 steel assessed by single edge notched tension tests
Margo Cauwels
Robin Depraetere
Wim De Waele
Stijn Hertelé
Kim Verbeken
Tom Depover
A1
Journal Article
in
INTERNATIONAL JOURNAL OF HYDROGEN ENERGY
2024
The effect of hydrogen and notch orientation in SENT specimens on the fracture toughness of an API 5L X70 pipeline steel
Robin Depraetere
Wim De Waele
Margo Cauwels
Tom Depover
Kim Verbeken
Stijn Hertelé
A1
Journal Article
in
ENGINEERING FRACTURE MECHANICS
2024
Damage evolution of a hydrogen charged grade X56 pipeline steel evaluated using X-ray micro-CT
Robin Depraetere
Wim De Waele
Margo Cauwels
Tom Depover
Kim Verbeken
Stijn Hertelé
C1
Conference
2024
Hydrogen-assisted degradation of an X70 pipeline steel evaluated by single edge notched tension testing
Margo Cauwels
Robin Depraetere
Wim De Waele
Stijn Hertelé
Tom Depover
Kim Verbeken
C1
Conference
2024
Hydrogen embrittlement of an X70 pipeline steel assessed by slow strain rate tensile tests
Margo Cauwels
Robin Depraetere
Wim De Waele
Stijn Hertelé
Kim Verbeken
Tom Depover
C3
Conference
2023
Hydrogen-assisted degradation of an X70 pipeline steel evaluated by single edge notched tension testing
Margo Cauwels
Robin Depraetere
Wim De Waele
Stijn Hertelé
Tom Depover
Kim Verbeken
C3
Conference
2023
Effect of stress triaxiality on the hydrogen embrittlement micromechanisms in a pipeline steel evaluated by fractographic analysis
Margo Cauwels
Robin Depraetere
Wim De Waele
Stijn Hertelé
Kim Verbeken
Tom Depover
A1
Journal Article
in
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
2023
Modeling of hydrogen-charged notched tensile tests of an X70 pipeline steel with a hydrogen-informed Gurson model
Robin Depraetere
Wim De Waele
Margo Cauwels
Tom Depover
Kim Verbeken
Stijn Hertelé
A1
Journal Article
in
MATERIALS
2023
Influence of stress triaxiality on hydrogen assisted ductile damage in an X70 pipeline steel
Robin Depraetere
Wim De Waele
Margo Cauwels
Tom Depover
Kim Verbeken
Matthieu Boone
Stijn Hertelé
A1
Journal Article
in
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
2023
Pipelines distribution : factors affecting material degradation during gaseous hydrogen transport
Aurélie Laureys
Robin Depraetere
Margo Cauwels
Stijn Hertelé
Kim Verbeken
Tom Depover
C3
Conference
2022
Effect of hydrogen charging on Charpy impact toughness of an X70 pipeline steel
Margo Cauwels
Robin Depraetere
Wim De Waele
Stijn Hertelé
Kim Verbeken
Tom Depover
P1
Conference
2022
Characterization of hydrogen-assisted degradation of a vintage and a modern pipeline steel
Margo Cauwels
Robin Depraetere
Wim De Waele
Stijn Hertelé
Tom Depover
Kim Verbeken
C3
Conference
2022
Characterization of hydrogen-assisted degradation of a vintage and a modern pipeline steel
Margo Cauwels
Robin Depraetere
Wim De Waele
Stijn Hertelé
Tom Depover
Kim Verbeken
C1
Conference
2022
Single edge notched tension testing for assessing hydrogen embrittlement : a numerical study of test parameter influences
Robin Depraetere
Wim De Waele
Margo Cauwels
Tom Depover
Kim Verbeken
Stijn Hertelé
C1
Conference
2022
Effect of hydrogen charging on Charpy impact toughness of two pipeline steels
Margo Cauwels
Robin Depraetere
Wim De Waele
Stijn Hertelé
Tom Depover
Kim Verbeken
C3
Conference
2022
Gaseous hydrogen transport in existing pipelines : a review of factors affecting material degradation
Aurélie Laureys
Robin Depraetere
Margo Cauwels
Tom Depover
Stijn Hertelé
Kim Verbeken
C1
Conference
2022
Ductile damage modelling of hydrogen assisted degradation in tensile and fracture toughness tests of X70 pipeline steel
Robin Depraetere
Wim De Waele
Stijn Hertelé
C1
Conference
2022
Influence of electrochemical hydrogenation parameters on microstructures prone to hydrogen-induced cracking
Margo Cauwels
Robin Depraetere
Wim De Waele
Stijn Hertelé
Tom Depover
Kim Verbeken
A1
Journal Article
in
JOURNAL OF NATURAL GAS SCIENCE AND ENGINEERING
2022
Use of existing steel pipeline infrastructure for gaseous hydrogen storage and transport : a review of factors affecting hydrogen induced degradation
Aurélie Laureys
Robin Depraetere
Margo Cauwels
Tom Depover
Stijn Hertelé
Kim Verbeken
A1
Journal Article
in
JOURNAL OF NATURAL GAS SCIENCE AND ENGINEERING
2022
Fully-coupled continuum damage model for simulation of plasticity dominated hydrogen embrittlement mechanisms
Robin Depraetere
Wim De Waele
Stijn Hertelé
A1
Journal Article
in
COMPUTATIONAL MATERIALS SCIENCE
2021
Hydrogen induced degradation of an X70 pipeline steel
Margo Cauwels
Robin Depraetere
Wim De Waele
Tom Depover
Stijn Hertelé
Kim Verbeken
C3
Conference
2021
Calibrating a ductile damage model for two pipeline steels : method and challenges
Robin Depraetere
Margo Cauwels
Wim De Waele
Tom Depover
Kim Verbeken
Stijn Hertelé
P1
Conference
2020